DIAGRAMAS PSO2 / PO2

(KELLOGG)

SISTEMA COBRE-AZUFRE-OXIGENO

Constantes de equilibrio para los diferentes equilibrios en el rango de 750 a 950 °K

Reacción log K = A/T +B

Equilibrios A B(1) 4CuO = 2Cu2O + O2 -14577 10.927

(2) 2Cu2O = 4Cu + O2 -17374 6.994

(3) Cu2S + O2 = 2Cu + SO2 11975 -2.139

(4) Cu2S + 3/2 O2 = Cu2O + SO2 20662 -5.636

(5) Cu2S + SO2 + 3O2 = 2CuSO4 59437 -38.501

(6) 2CuS + O2 = Cu2S + SO2 20459 -5.126

(7) CuS + 2O2 = CuSO4 39951 -21.816

(8) 2CuSO4 = Cu2O + 2SO2 + 3/2 O2 -38780 32.872

(9) 2CuSO4 = CuO.CuSO4 + SO2 + 1/2 O2 -15844 14.151

(10) CuO.CuSO4 = 2CuO + SO2 + 1/2 O2 -15641 13.249

(11) CuO.CuSO4 = Cu2O + SO2 + O2 -22932 18.716

20-2-4-6-8

12

10

8

6

4

2

0

-2

Cu-O -S Phase Stability Diagram at 1000.000 C

File: C:\HSC6\Lpp\CuOS1000.ips log pO2(g)

log pSO2(g)

CuCuO

Cu2O

CuS

Cu2S

CuSO4

-4-5-6-7-8-9-10-11-12

7

6

5

4

3

2

1

0

-1

-2

-3

Ni-O -S Phase Stability Diagram at 1000.000 C

File: C:\HSC6\Lpp\NiOS1000.ips log pO2(g)

log pSO2(g)

Ni

NiO

NiS

NiSO4

1.- Ni + ½ O2(g) = NiO

2.- Ni + SO2(g) = NiS + O2(g)

3.- NiS + 2O2(g) = NiSO4

4.- NiO + SO2(g) + ½ O2(g) = NiSO4

5.- NiO + SO2(g) = NiS + 1 ½ O2(g)

SISTEMA NIQUEL-AZUFRE-OXIGENO

Constantes de equilibrio para los diferentes equilibrios a una temperatura de 1000 °K

Equilibrios Log K

1.- Ni + ½ O2 = NiO 7.6664

2.- Ni3S2 + 2O2 = 3Ni + 2SO2 21.393

3.- 3NiS + O2 = Ni3S2 + SO2 12.2305

4.- NiS + 1½O2 = NiO + SO2 18.8742

5.- NiS + 2O2 = NiSO4 21.5972

6.- NiO + SO2 + ½O2 = NiSO4 2.723

0-4-8-12-16-20

15

10

5

0

-5

-10

-15

-20

Zn-O -S Phase Stability Diagram at 1000.000 C

File: C:\HSC6\Lpp\ZnOS1000.ips log pO2(g)

log pSO2(g)

Zn

ZnO

ZnS

ZnSO4

Sistema Zn-S-O a 900 K

a) ZnS + 2O2 = ZnSO4 Log K = 26.61

b) 3ZnSO4 = ZnO 2ZnSO4 + SO2 + 1/2 O2 Log K = -3.98

c) 3ZnS + 11/2 O2 = ZnO 2ZnSO4 + SO2 Log K = 75.84

d) ZnO 2 ZnSO4 = 3ZnO + 2SO2 + O2 Log K = -10.52

e) ZnS + 3/2 O2 = ZnO + SO2 Log K = 21.77

f) Zn + SO2 = ZnS + O2 Log K = -6.85

g) 2Zn + O2 = 2ZnO Log K = 29.84